产品参数
PETG韩国SKK2012 物性数据表
·
|
性能项目 |
测试条件 |
测试方法 |
数值/描述 |
单位 |
|
|
机械性能 |
拉伸强度(引张强度) |
|
ASTM D412/ISO 527 |
|
kg/cm2(MPa)[Lb/in2] |
|
断裂伸长率 |
|
ASTM D412/ISO 527 |
70 |
% |
|
|
拉伸模量 |
|
ASTM D412/ISO 527 |
|
kg/cm2(MPa)[Lb/in2] |
|
|
拉伸屈服伸长率(延伸率) |
|
ASTM D412/ISO 527 |
|
% |
|
|
拉伸断裂伸长率(延伸率) |
|
ASTM D412/ISO 527 |
|
kg/cm2(MPa)[Lb/in2] |
|
|
弯曲模量(弯曲弹性率) |
|
ASTM D790/ISO 178 |
2150 |
kg/cm2(MPa)[Lb/in2] |
|
|
弯曲强度 |
|
ASTM D790/ISO 178 |
80 |
kg/cm2(MPa)[Lb/in2] |
|
|
洛氏硬度 |
|
ASTM D785 |
116 |
kg·cm/cm(J/M)ft·lb/in |
|
|
IZOD 缺口冲击强度 |
1/4" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
|
|
1/4" -30℃ |
ASTM D256/ISO 179 |
|
kg/cm2(MPa)[Lb/in2] |
||
|
1/8" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
1/8" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
Charpy冲击强度 |
23℃ （缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
|
|
-30℃（缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
23℃（无缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
-30℃（无缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
物性性能 |
比重（密度） |
|
ASTM D792/ISO 1183 |
1.27 |
|
|
成型收缩率 |
|
ASTM D955 |
0.2 |
% |
|
|
光学性能 |
折射率 |
|
ASTM D542/ISO 489 |
1.570 |
|
|
透光率 |
|
ASTM D1003/ISO 13468 |
89.0 |
% |
|
|
模糊系数（Haze） |
|
ISO 14782 |
|
% |
|
|
其他 |
备注 |
|
|||
|
颜色 |
GT |
||||
|
特性 |
高光泽，耐化学，食品级，韧性良好，可加工性良好 |
||||
|
用途 |
电气/电子应用领域，护罩，玩具，片材，瓶子，医疗/护理领域 |
||||
3D打印专用材料/韩国SK PETG K2012
韩国SK PETG K2012 是3D打印的专用材料
出众的热成型性能
PETG板材易于生产出造型复杂及拉伸比大的制品。而且，与PC板和抗冲改性的压克力不同，这种板材无须在热成型加工前进行预干燥处理。与PC板或压克力相比，其成型周期短，温度低，成品率更高。
坚韧性
PETG板材的挤出板材通常比通用压克力坚韧15至20倍，比抗冲改性的压克力坚韧5至10倍。PETG板材在加工、运输和使用过程中具有足够的承受能力，有助于防止破裂。
耐候性
PETG板材提供了的耐候性。它可以保持产品的坚韧性，防止变黄。它含有紫外线吸收剂，可共挤成一保护层，保护了板材免受紫外线的有害影响。
加工简便
PETG板材可进行锯切、模切、钻孔、冲孔、剪切、铆接、铣边以及冷弯，不至于破碎。表面的轻微刮痕可用热风枪来消除。溶剂粘接亦是常规操作。它比通用压克力、抗冲改性压克力或PC板更易于加工，并可进行植绒、电镀、静电等加工处理。
的耐化学性能
PETG板材可以耐受多种化学品以及常用的清洁剂。
环保
PETG板材基材均为环保材料，符合食品接触管理要求。
经济性
它比PC板便宜，比压克力经久耐用。